Study of Fatigue Fractography of Mild Steel Used in Automotive Industry
DOI:
https://doi.org/10.22153/kej.2019.07.003Keywords:
Automotive, fatigue, fracture, mild steel.Abstract
Fatigue failure is almost considered as the predominant problem affecting automotive parts under dynamic loading condition. Thus, more understanding of crack behavior during fatigue can strongly help in finding the proper mechanism to avoid the final fracture and extent the service life of components. The main goal of this paper is to study the fracture behavior of low carbon steel which is used mostly in automotive industry. For this purpose, the fractography of samples subjected to high and low stress levels in fatigue test then was evaluated and analyzed. Hardness and tensile tests were carried out to determine the properties of used steel. Also, the samples were characterized by microstructure test and XRD analysis to examine the constitute phases. The fatigue test (S-N curve) was done at stress ratio (R= -1), and the fracture examination was perform using Scanning Electron Microscope (SEM). The results of microstructure and XRD analysis were indicating that the Ferrite and a little amount of pearlite are the dominant phases of this steel. Whereas, the fractography observations reveal that the void coalescence ductile fracture is the main failure mode in samples with high stress level, while the ductile fracture (void coalescence) with Transgranular Cleavage fracture was noticed in low stress fatigue mode for this alloy.
Downloads
Published
Issue
Section
License
Copyright: Open Access authors retain the copyrights of their papers, and all open access articles are distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution and reproduction in any medium, provided that the original work is properly cited. The use of general descriptive names, trade names, trademarks, and so forth in this publication, even if not specifically identified, does not imply that these names are not protected by the relevant laws and regulations. While the advice and information in this journal are believed to be true and accurate on the date of its going to press, neither the authors, the editors, nor the publisher can accept any legal responsibility for any errors or omissions that may be made. The publisher makes no warranty, express or implied, with respect to the material contained herein.