Abstract
In this work, yttrium oxide particles (powder) reinforced AL-Si matrix composites (Y2O3/Al-Si) and Chromium oxide particles reinforced AL-Si matrix composites (Cr2O3/AL-Si) were prepared by direct squeeze casting. The volume percentages of yttrium oxide used are (4, 8.1, 12.1, 16.1 vol %) and the volume percentages of the chromium oxide particles used are (3.1, 6.3, 9.4, 12.5 vol. %). The parameters affecting the preparation of Y2O3/Al-Si and Cr2O3/AL-Si composites by direct squeeze casting process were studied. The molten Al-Si alloy with yttrium oxide particles or with chromium oxide particles was stirred again using an electrical stirrer at speed 500 rpm and the molten alloy was poured into the squeeze die cavity. The pouring temperature that used for all castings is (700)˚C. The required squeeze pressure, 53 MPa, was then applied for 30 seconds at a delay time of 5. The die temp is (200˚C). The Y2O3/Al-Si composites and Cr2O3/Al-Si composites produced by squeeze casting have more microstructure refinement, higher hardness and lower wear rate than the unreinforced alloy.
References
[2] Hong C.P., Shen H.F., Cho I.S., “Prevention of macrosegregation in squeeze casting of an Al-4.5wt Cu alloy” Met. Mat. Trans., vol. 29A, Jan. 1998, pp. 339-349.
[3] Long S., Beffort O., Moret G., Thevoz Ph., “Processing of Al-based MMCs by indirect squeeze infiltration of ceramic performs on a shot-control high pressure die casting machine” J. Mat. Sci. Eng., 1999, pp. 1-10.
[4] Prakasan K., Seshan S., “Microstructure and properties of squeeze cast Cu/carbon fiber metal matrix composite” J. Mat. Sci., vol. 34, 1999, pp. 5045-5049.
[5] Zhang X.X., Wang D.Z., Geng L.,“Coarsening of eutectic silicon in squeeze cast alumina fiber reinforced eutectic Al-Si aluminum composites” J. Mat. Sci. Lett., vol. 22, 2003, pp. 861-863.
[6] Etter T., Kuebler J., Frey T., Schulz P., Loffler J.F., Uggowitzer P.J., “Strength and fracture toughness of interpenetrating graphite/aluminum composites produced by the indirect squeeze casting process” Mat. Sci. Eng, vol. A386, 2004, pp. 61-67.
[7] Long S., Beffort O., Caron C., Bonjour C., “Microstructure and mechanical properties of a high volume fraction SiC particle reinforced AlCu4MgAg squeeze casting” J. Mat. Sci. Eng., vol. A, 1999, pp. 1-23.
[8] Kiourtsidis G., Skolianos S.M., “Corrosion behavior of squeeze-cast silicon carbide-2024 composites in aerated 3.5 wt٪ sodium chloride” J. Mat. Sci. Eng., vol. A248, 1998, pp. 165-172.
[9] Hufnagel W., “Key to Aluminum alloys” Aluminum-Verlag, Düsseldorf, 1982, p. 119.
[10] Maleki A., Niroumand B., Shafyei A., “Effects of squeeze casting parameters on density, macrostructure and hardness of LM13 alloy” Mat. Sci. Eng., vol. A428, 2006, pp. 135-140.
[11] Takhakh A.M., “Solidification simulation and experimental investigation of Al-Si cast structures” Ph.D. thesis, Department of Production Engineering and Metallurgy, University of Technology, Baghdad, Iraq, 2007.
[12] Bolton W., “Engineering materials technology” Third edition, Butterworth Heinemann, 1998, p. 4.
[13] Meyers M.A., Chawla K.K., “Mechanical behavior of materials” Prentice-Hall, Inc., USA, 1999, p. 644.
[14] Abtan N.S., “A study on squeeze casting parameters effects on improving the metallurgical and mechanical properties of aluminum alloys” Ph.D. thesis, Dept. of Production Engineering and Metallurgy, University of Technology, Baghdad, Iraq, 2007.
[15] Callister W.D.Jr., “Materials science and engineering, An introduction” Fifth edition, John Wiley & Sons, Inc., 2000, p. 136.
[16] Al-Kaaby A.S.J., “Preparation and characterization of cast aluminum matrix SiC particulate composite” Ph.D. thesis, Department of Production Engineering and Metallurgy, University of Technology, Baghdad, Iraq, Nov. 2000.
[17] Rooy E.L., “Aluminum and aluminum alloys” ASM Metals Handbook, casting, 9th edition, 4th printing, vol. 15, Materials park, OH, 1998.
[18] Long S, Beffort O., Cayron C., Bonjour C., “Microstructure and mechanical properties of a high volume fraction SiC particle reinforced AlCu4MgAg squeeze casting” Mat. Sci. Eng., vol. A, 1999.
Copyright: Open Access authors retain the copyrights of their papers, and all open access articles are distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution and reproduction in any medium, provided that the original work is properly cited. The use of general descriptive names, trade names, trademarks, and so forth in this publication, even if not specifically identified, does not imply that these names are not protected by the relevant laws and regulations. While the advice and information in this journal are believed to be true and accurate on the date of its going to press, neither the authors, the editors, nor the publisher can accept any legal responsibility for any errors or omissions that may be made. The publisher makes no warranty, express or implied, with respect to the material contained herein.