In this study, NaOH dissolution method was applied to dissolve cellulose fibers which extracted from date palm fronds (type Al-Zahdi) taken from Iraqi gardens. In this process, (NaOH)-solution is brought into contact with the cellulose fibers at low temperature. Experiments were conducted with different concentrations of NaOH (4%, 6%, 8% and12%) weight percent at two cooling bath temperatures (-15 oC) and (-20oC). Maximum cellulose dissolution was 23 wt% which obtained at 8 wt% concentration of NaOH and at cooling bath temperature of -20oC. In order to enhance the cellulose fibers dissolution, the sample was pretreated with Fenton's reagent which consists of hydrogen peroxide (H2O2), oxalic acid (C2H2O4) and ferrous sulfate (FeSO4). This reagent reacts with cellulose fibers and produces free radicals which increase cellulose dissolution. In this work three variables were studied: cooling bath temperature (-15oCand-20oC), NaOH concentration (4%, 6%, 8% and12%) and time of Fenton's reagent treatment (1-48) hrs. The results showed that the best percent of cellulose dissolution was (42 wt %) which occurred at treatment time (24 hours), temperature (-20oC) and NaOH concentration 8%. In another set of experiments urea was added to NaOH solution as a catalyst with proportion (6%NaOH+4% urea) at two temperatures -15 and -20 oC. The results show that the solubility of cellulose increase to 62% for the sample which treated with Fenton's reagent and to 35% for the untreated sample, both values were obtained at -15oC.
Copyright: Open Access authors retain the copyrights of their papers, and all open access articles are distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution and reproduction in any medium, provided that the original work is properly cited. The use of general descriptive names, trade names, trademarks, and so forth in this publication, even if not specifically identified, does not imply that these names are not protected by the relevant laws and regulations. While the advice and information in this journal are believed to be true and accurate on the date of its going to press, neither the authors, the editors, nor the publisher can accept any legal responsibility for any errors or omissions that may be made. The publisher makes no warranty, express or implied, with respect to the material contained herein.